Acier doux 1018
Type de matériau
Métal
Nom du matériau
Acier doux 1018
Noms alternatifs
G10180 | AISI 1018
Compatibilité des processus
Fraisage CNC, Tournage CNC
Acier doux 1018 dans le domaine de l'usinage CNC
L'acier doux 1018, connu sous le nom d'acier à faible teneur en carbone, peut être facilement percé, tourné, fraisé et taraudé.
It is composed of Carbon (C) within the range of 0.15-0.20%, Manganese (Mn) at 0.60-0.90%, with maximum limits of 0.04% for Phosphorus (P) and 0.05% for Sulfur (S). These elements contribute to its excellent machinability. In CNC machining 1018, we use sharp cutting tools to maintain a good surface finish. We optimize cutting speeds and feeds based on the specific CNC machine and tooling. We also use coolant/lubrication to control heat during machining. We also consider the workpiece's geometry and fixturing for stability.
It is more machinable than lower-carbon steel. We offer 1018 steel in various forms, including cold-rolled steel, bars, sheets/plates, and wire. Cold-rolled steel is known for its smooth finish, while steel bars are versatile and used for bolts and axles. Sheets/plates are flat and suitable for welding in manufacturing, and steel wire, due to its weldability, is commonly used in construction projects and for crafting items like springs and fencing.
Tableau des propriétés of Mild Steel 1018
| PROPRIÉTÉS MÉCANIQUES | |
|---|---|
| Résistance ultime à la traction | 380-450 MPa |
| Limite d'élasticité | 220-350 MPa |
| Module de Young (élasticité) | 190-205 GPa |
| Allongement à la rupture | 13-25 % |
| Propriétés physiques | |
| Résistance à la corrosion | Pauvre |
| Magnétisme | Semi-magnétique |
| Résistance aux UV | Résistance limitée aux UV |
| Soudabilité | Excellent weldability with proper procedures |
| Propriétés thermiques | |
| Température de service maximale | Approximately 400°C(752°F) |
| Coefficient de dilatation thermique | 11.5-12 x 10^-6/°C |
| Conductivité thermique | 52 W/(m·°C) |
| Propriétés électriques | |
| Résistivité électrique | 16-18 μΩ*cm |
| Sécurité ESD | Non |
Connaissances de base of Mild Steel 1018
What is Mild Steel 1018?
1018 steel is a high-manganese carbon alloy known for excellent machinability. It's preferred for carburized parts due to uniform, hard cases from welds.
1018 is manufactured by melting iron, carbon, and manganese in an electric air and basic oxygen furnace. The molten metal is cast into slabs, then hot-rolled or shaped above its recrystallization temperature. Forging and annealing involve cold working (e.g., cold drawing, rolling, forging) to enhance strength. Heat treatment, commonly annealing, is for improved hardness and durability.
Advantages of Mild Steel 1018
Highly weldable
Excellente usinabilité
Rentabilité
Polyvalence
Good ductility
Responds well to heat treatment
Largement disponible
Applications of Mild Steel 1018
Bolts and nuts
Engrenages
Arbres
Composants automobiles
Matériaux de construction
General engineering parts
Machining Mild Steel 1018 FAQ sur l'achat
Autres Matériaux
Cuivre
Le cuivre est un excellent choix pour le câblage électrique et l'électronique. C'est un excellent conducteur d'électricité et de chaleur. En outre, il est durable et facile à façonner.
Aluminium
L'aluminium est l'un des métaux les plus utilisés au monde en raison de son excellent rapport résistance/poids, de son faible coût et de sa recyclabilité.
Acier allié
Plus puissant que l'acier au carbone, plus résistant à l'usure, plus résistant à la déchirure. L'acier allié est durable et peut résister à des environnements à haute température.