Latão 260
Tipo de material
Metal
Nome do material
Latão 260
Nomes alternativos
C26000 | CuZn30 | CZ106 | Cartridge Brass
Compatibilidade de processos
Fresagem CNC, Torneamento CNC
Latão 260 em Maquinação CNC
Brass 260, also known as Cartridge Brass, is composed of approximately 70% copper and 30% zinc.
It has excellent machinability and produces small, fine chips during machining, and the material doesn't tend to gum up the cutting tools. Brass is typically machined at higher cutting speeds compared to steel. However, the specific speeds and feeds will depend on the CNC machine's capabilities, the type of cutting tool, and the complexity of the part being machined.
Brass has a naturally attractive golden color and can be machined to achieve a smooth surface finish. The machined parts may require additional processes like polishing or coating if a specific finish is desired. Moreover, aside from being corrosion-resistant, brass 260 has good dimensional stability and can hold tight tolerances.
Tabela de propriedades of Brass 260
| PROPRIEDADES MECÂNICAS | |
|---|---|
| Resistência à tração final | 390 MPa |
| Resistência ao escoamento | 345 MPa |
| Módulo de Young (Elasticidade) | 97 GPa |
| Alongamento na rutura | 40% |
| Dureza | 80 HRB(Rockwell B) |
| Propriedade física | |
| Resistência aos raios UV | Good resistance |
| Propriedade térmica | |
| Temperatura máxima de serviço | 300°C(572°F) |
| Coeficiente de expansão térmica | 19 x 10^-6/°C |
| Condutividade térmica | 109 W/(m·K) |
| Propriedade eléctrica | |
| Segurança ESD | Boa condutividade eléctrica |
Conhecimentos básicos of Brass 260
What is Brass 260?
Latão 260 is a popular and cost-effective brass alloy. It is highly ductile and possesses good strength, finishing abilities, and corrosion resistance. It can be easily machined and cold-formed. However, it's unsuitable for projects involving contact with acetic acid, hydrochloric acid, nitric acid, or ammonia. Avoid soldering due to its high zinc content.
Furthermore, it has an appealing smooth, yellow brass finish that can be polished to a gold-like appearance or brushed satin finish. Unlike steel and iron, brass 260 forms a thin protective patina, preventing rust when exposed to the atmosphere. It is commonly used in architecture, electrical parts, fasteners, and ammunition casings.
Advantages of Brass 260
Easy to machine for various processes
Boa formabilidade
Good Corrosion Resistance
Easily cold worked for enhanced strength and hardness
Aesthetic Appeal
Biocompatibilidade
Superior electrical conductivity
Low thermal conductivity
Applications of Brass 260
Conectores eléctricos
Musical instruments (e.g., trumpets, trombones)
Plumbing fittings (e.g., valves)
Decorative items (e.g., jewelry, ornaments)
Automotive parts (e.g., radiator cores)
Clock and watch components
Lock and key components
Fasteners (e.g., nuts, bolts)
Machining Brass 260 FAQs sobre a compra
Outros Materiais
Latão Cz121
Brass CZ121 é a designação de um tipo de liga de latão. O latão é uma liga metálica constituída principalmente por cobre e zinco.
Latão C360
O latão C360, também conhecido como latão de corte livre ou latão com chumbo, é uma liga composta principalmente por cobre e zinco, com uma pequena percentagem de chumbo.
Latão 260
O latão 260 é uma liga de latão popular e económica. É altamente dúctil e possui boa força, capacidade de acabamento e resistência à corrosão.
Obter um orçamento exato Para os seus próximos projectos
Independentemente de o seu projeto ser complicado ou simples, de ser de metal ou de plástico, receberá um orçamento preciso no prazo de 6 horas.