Unlegierter Stahl 1018
Material Typ
Metall
Material Name
Unlegierter Stahl 1018
Alternative Namen
G10180 | AISI 1018
Prozess-Kompatibilität
CNC-Fräsen, CNC-Drehen
Unlegierter Stahl 1018 in der CNC-Bearbeitung
Der als kohlenstoffarmer Stahl bekannte Baustahl 1018 lässt sich leicht bohren, drehen, fräsen und gewinden.
It is composed of Carbon (C) within the range of 0.15-0.20%, Manganese (Mn) at 0.60-0.90%, with maximum limits of 0.04% for Phosphorus (P) and 0.05% for Sulfur (S). These elements contribute to its excellent machinability. In CNC machining 1018, we use sharp cutting tools to maintain a good surface finish. We optimize cutting speeds and feeds based on the specific CNC machine and tooling. We also use coolant/lubrication to control heat during machining. We also consider the workpiece's geometry and fixturing for stability.
It is more machinable than lower-carbon steel. We offer 1018 steel in various forms, including cold-rolled steel, bars, sheets/plates, and wire. Cold-rolled steel is known for its smooth finish, while steel bars are versatile and used for bolts and axles. Sheets/plates are flat and suitable for welding in manufacturing, and steel wire, due to its weldability, is commonly used in construction projects and for crafting items like springs and fencing.
Tabelle Eigenschaften of Mild Steel 1018
| MECHANISCHE EIGENSCHAFTEN | |
|---|---|
| Zugfestigkeit (Ultimate Tensile Strength) | 380-450 MPa |
| Streckgrenze | 220-350 MPa |
| Elastizitätsmodul (Elastizität) | 190-205 GPa |
| Dehnung beim Bruch | 13-25 % |
| Physikalische Eigenschaften | |
| Korrosionsbeständigkeit | Schlecht |
| Magnetismus | Halbmagnetisch |
| UV-Beständigkeit | Begrenzte UV-Beständigkeit |
| Schweißeignung | Excellent weldability with proper procedures |
| Thermische Eigenschaften | |
| Maximale Betriebstemperatur | Approximately 400°C(752°F) |
| Wärmeausdehnungskoeffizient | 11.5-12 x 10^-6/°C |
| Wärmeleitfähigkeit | 52 W/(m·°C) |
| Elektrische Eigenschaften | |
| Elektrischer spezifischer Widerstand | 16-18 μΩ*cm |
| ESD-Sicherheit | Nein |
Grundkenntnisse of Mild Steel 1018
What is Mild Steel 1018?
1018 steel is a high-manganese carbon alloy known for excellent machinability. It's preferred for carburized parts due to uniform, hard cases from welds.
1018 is manufactured by melting iron, carbon, and manganese in an electric air and basic oxygen furnace. The molten metal is cast into slabs, then hot-rolled or shaped above its recrystallization temperature. Forging and annealing involve cold working (e.g., cold drawing, rolling, forging) to enhance strength. Heat treatment, commonly annealing, is for improved hardness and durability.
Advantages of Mild Steel 1018
Highly weldable
Ausgezeichnete Bearbeitbarkeit
Kostengünstig
Vielseitigkeit
Gute Duktilität
Responds well to heat treatment
Weithin verfügbar
Applications of Mild Steel 1018
Bolts and nuts
Zahnräder
Schächte
Komponenten für die Automobilindustrie
Baumaterialien
General engineering parts
Machining Mild Steel 1018 FAQs zum Kauf
Andere Materialien
Kupfer
Kupfer ist die erste Wahl für elektrische Leitungen und Elektronik. Es ist ein hervorragender Leiter für Strom und Wärme. Außerdem ist es haltbar und leicht zu formen.
Aluminium
Aluminium ist aufgrund seines hervorragenden Verhältnisses von Festigkeit zu Gewicht, seiner geringen Kosten und seiner Recyclingfähigkeit eines der am häufigsten verwendeten Metalle der Welt.
Legierter Stahl
Leistungsfähiger als Kohlenstoffstahl, verschleißfester, reißfester. Legierter Stahl ist langlebig und kann hohen Temperaturen standhalten.
Genaues Angebot einholen Für Ihre nächsten Projekte
Ganz gleich, ob Ihr Projekt kompliziert oder einfach ist, ob es sich um Metall oder Kunststoff handelt, Sie erhalten innerhalb von 6 Stunden ein genaues Angebot.
Heute ein Angebot einholen